- Zinc Polycarboxylate based multipurpose cement
- Low film thickness with high adhesive strength
- Minimal solubility in oral fluids
PACKAGING
- Intro Pack : 1 x 30g Powder Jar, 1 x 15ml Liquid Bottle,1 x Spoon, 1 x Mixing Pad, 1 x Instruction Manual
Poly Zinc+
Zinc Polycarboxylate Cement
₹450.00
CE 0123
The product is audited & approved as per European standards and laws, and has a valid CE Certifications
MDSAP
MDSAP quality management system satisfies the regulatory jurisdictions requirements of MDSAP Countries.
CDSCO
Registered & Approved as per MDR 2017 Guidelines by Central Drugs Standard Control Organization
INDICATIONS
- Suitable for cementation of : Crowns, bridges and orthodontic brackets
- Cavity lining under all restoration materials
- Temporary fillings and fillings of deciduous teeth
PRODUCT BENEFITS
- Chemically bonds to tooth structure and metal appliances
- Extremely low film thickness
- Radiopaque
- High adhesive strength
- Minimal solubility in oral fluids
| Technical Data | Standard Applied | |
|---|---|---|
| 1. Mixing Time | 45-60 Sec. | ISO 9917-1 |
| 2. Setting Time | 2 – 2:15 min. (Luting) 2 – 2:10 min. (Base) |
|
| 3. Film Thickness | 25 μm | |
| 4. Compressive Strength | 50 Mpa (Min.) |
Size30g Pow+15ml Liq
3 reviews for Poly Zinc+
Instructions for Use : Shake Powder bottle before use: Dispense 2 spoons full of powder and 3-4 drops of liquid on a glass mixing slab or mixing pad. Thoroughly rinse the tooth surface with water and gently air dry. Mix powder and liquid for45- 60secs to a smooth paste. Thinly apply Poly Zinc+ over the tooth structure and the interfacing metal surfaces before they are joined. For maximum bond strength Poly Zinc + must be allowed to set 2:00 to2:15(min-sec) while metal and prepared tooth surfaces are compressed together. For this it is advised that the patient bites hard onto a cotton ball without periodic relaxation. Biting hard will remove excess cement and reduce its film thickness and improve the bond.
Warning : Avoid prolonged or repeated contact with skin (allergic contact dermatitis), and eyes. Avoid prolonged inhalation. Do not take internally Contact with the skin may cause irritation, burns of hypersensitivity. If contact with skin occurs immediately wipe off thoroughly with cotton and alcohol and then wash well with soap and water. If skin rash and sensitization or other allergic reaction occurs discontinue use and seek medical attention. If the product comes into contact with the eyes, rinse thoroughly with fresh water and consult a physician. It should not be used with patients who have a history of severe allergic reaction to any of the components.
Contraindications : Direct or indirect pulp-capping.
Caution : After dispensing, replace the caps of the powder jar and liquid bottle. Store both in a cool and dark place.
Storage Conditions : Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life is not affected after opening if stored in a cool dry place.
Shelf Life : 3 years from the date of manufacturing.
Anup –
Poly Zinc+ is an exceptional zinc polycarboxylate cement that proves highly versatile for various dental applications, including permanent restorations, crowns, and bases. Its adaptability makes it a reliable choice for many procedures, accommodating different clinical situations effectively.
Patrick –
The mixing and application process is quite user-friendly. The consistency is smooth and easy to manipulate, allowing for precise placement. However, some users may need to practice to achieve the ideal mix for optimal setting properties, but overall, it’s straightforward and manageable.
Sarang –
One of the standout features of Poly Zinc+ is its excellent adhesion to both tooth structure and restorative materials. The cement provides a strong bond that minimizes the risk of microleakage and enhances the longevity of restorations. I’ve consistently seen fewer issues with sensitivity and dislodgment in my patients.